TPE Breast Reduction at Reverend Jacks
- Wheezer
- Doll Elder
- Posts: 2545
- Joined: Sat Dec 22, 2018 1:49 am
- Location: Wheezerville, USA
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
But every repair has some bumpy bits.
Interesting use of the ropes.
You might have a future in the bondage groups.
Keep up the efforts.
Cheers!
... W ...
Re: TPE Breast Reduction at Reverend Jacks
Hoping for a better outcome with the thicker paste Rev
- Hot doll reviews
- Doll Mentor
- Posts: 1128
- Joined: Thu Jan 20, 2022 8:08 pm
- Location: My Harem Tent in My Desert Kingdom 🏜️ 🌵🧚🏼♀️🧚🏼♀️🧚🧚♂️💃👙🩴👗🌹🧘♀️
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
- soonpk
- Doll Mentor
- Posts: 1252
- Joined: Fri Jan 06, 2012 1:01 pm
- Location: Northern California
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
Re: TPE Breast Reduction at Reverend Jacks
Aside comment: When I paste the split in vaginas, I close the legs on the repair until the cure is done. The whole time there is a constant positive pressure so any fluid-dynamics caused migration of TPE is into the healing wound, not out. I am convinced that TPE acts as a superthick fluid, which is why it you put her arm straight up then down nothing bad happens. Place her arm up and leave it there, eventually it will tear.
So I decided to take a new tact, and try out a new toy, and I'm sealing the seams with heat. Here's my new toy: The foot is long enough to penetrate deep into the seam, so let's try and see if old Rev Jack can use the damn thing...
ALSO TRY Reverend Jack's Anointed Snake Oil, good for cleansing stains from the body and the Soul! Step right up folks, only $5 a bottle! We got plenty to go around! Cash only please.
Aibei 158 Blue Elf, AS 157, XES 128, OR 156G, WM 160C (r), Sanhui 168 (r), WM 157B, WM 138D (Faun), Mistress 168 (r), 6YE 100 (Bubbles)
Re: TPE Breast Reduction at Reverend Jacks
So I'm not fucking Wheezer, or Morghana the doll witch. (Although given a shot a Morghana I might take it). But here's a titty anyway: Yep, kinda pointy and not quite round yet, I'm working on it.
LOTS OF LESSONS LEARNED ON THIS ONE! But that's my point, I fuck it up so you don't have to!
I got souls to save so I have to run for now... More later.
Reverend Jack
ALSO TRY Reverend Jack's Anointed Snake Oil, good for cleansing stains from the body and the Soul! Step right up folks, only $5 a bottle! We got plenty to go around! Cash only please.
Aibei 158 Blue Elf, AS 157, XES 128, OR 156G, WM 160C (r), Sanhui 168 (r), WM 157B, WM 138D (Faun), Mistress 168 (r), 6YE 100 (Bubbles)
Re: TPE Breast Reduction at Reverend Jacks
Persistent though, and apparently a prolific cusser
- Wheezer
- Doll Elder
- Posts: 2545
- Joined: Sat Dec 22, 2018 1:49 am
- Location: Wheezerville, USA
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
EEK !!!RevJack wrote: ↑Mon Aug 21, 2023 3:50 pm My dearest flock, it appears that your poor Reverend has trouble doing multiple things at one time. So you get no pictures. Sorry. Good news, you didn't have to hear all the cussin' either!
So I'm not fucking Wheezer, or Morghana the doll witch. (Although given a shot a Morghana I might take it). But here's a titty anyway:
....
Reverend Jack
Many thanks RevJack for not fucking me !
I do appreciate the thought, however I do not swing that way.
(But perhaps that is not what you meant exactly)
A fluid comparison is a close to TPE, it appears solid but still slightly flows. Sort of like how glass appears solid but will flow over time. Witness certain original Colonial era windows in US structures.RevJack wrote: ↑Mon Aug 21, 2023 3:36 pm Aside comment: When I paste the split in vaginas, I close the legs on the repair until the cure is done. The whole time there is a constant positive pressure so any fluid-dynamics caused migration of TPE is into the healing wound, not out. I am convinced that TPE acts as a superthick fluid, which is why it you put her arm straight up then down nothing bad happens. Place her arm up and leave it there, eventually it will tear.
From what I have seen it really gets down to tension and compression reaction of the TPE material. Consider that the material has partial bonding which results is softness at the expense of rigidity (such as silicone). So under compression the TPE is fine, yet under tension (or stress) these partial bonds do not hold well over time. Most materials do better in compression than tension.
Your new Heated Blade of TPE Repair should also work quite well with your paste.
I have observed that a TPE area bonded with uncured chemicals (3M, xylene, etc,) or uncured TPE paste will exhibit a melt point LOWER that the raw TPE material.
You can use that to your advantage here by using paste first then inserting the heated knife to "melt" the paste to flow and fill in all the internal voids and crevices.
It will also accelerate curing.
Looking good so far, it appears the heated blade is a timely tool addition.
Cheers!
... W ...
Re: TPE Breast Reduction at Reverend Jacks
You're exhaust ports are safe, the reference was my frustration that when The Good Lord was handing out TPE molding, modding, and smoothing skills, he gave you yours, then mine, then had you and Morghana get back in line again.
Returning to my equine references, it seems the only TPE texture I can adequately reproduce is donkey balls.
Reverend Jack
ALSO TRY Reverend Jack's Anointed Snake Oil, good for cleansing stains from the body and the Soul! Step right up folks, only $5 a bottle! We got plenty to go around! Cash only please.
Aibei 158 Blue Elf, AS 157, XES 128, OR 156G, WM 160C (r), Sanhui 168 (r), WM 157B, WM 138D (Faun), Mistress 168 (r), 6YE 100 (Bubbles)
- Wheezer
- Doll Elder
- Posts: 2545
- Joined: Sat Dec 22, 2018 1:49 am
- Location: Wheezerville, USA
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
Thanks for the reassurance, I now feel better. And the kind words are appreciated.
However lack of a final smooth surface may not be a major issue.
Apparently there is an interest HERE (viewtopic.php?p=2405380) for dolls with cellulite, lard ripples, stretch marks and body pockmarks.
Thus there seems to be interest by some folks for dolls with donkey balls skin texture.
Fair warning, if you go to that link there are images that you can not unsee and that might haunt you.
Keep up the efforts.
Cheers!
... W ...
- Hot doll reviews
- Doll Mentor
- Posts: 1128
- Joined: Thu Jan 20, 2022 8:08 pm
- Location: My Harem Tent in My Desert Kingdom 🏜️ 🌵🧚🏼♀️🧚🏼♀️🧚🧚♂️💃👙🩴👗🌹🧘♀️
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
PS- by the way if I recall, there were some episodes of nip/tuck with a doll star appearing in them. IDK any input on who the doll was?
- homersexual
- Senior Member
- Posts: 499
- Joined: Wed Jun 16, 2004 12:00 am
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
This is an interesting and encouraging thread. Wheezer is right about bonding and curing, at least with my WM that has been the case. I find that the TPE is too soft for heat to work in most cases, and manipulating any paste I've made depends on consistency, but the tension areas are the worst and tend to require a lot more touch up and retouching.
That's been my experience with Vagina reconstruction. What has been the most effective is a TPE paste and some kind of object to keep the shape and provide opposing pressure to the TPE in the cavity against the partially closed legs. I keep my doll inverted, and the neutral internal pressure causes the TPE paste to creep into the surface fissures and bond, and the excess is pushed up out of the cavity and settles. I have used lots of TPE for this approach so that the legs don't have to be closed all the way and some of the tension is relieved.RevJack wrote: ↑Mon Aug 21, 2023 3:36 pm *snip*
Aside comment: When I paste the split in vaginas, I close the legs on the repair until the cure is done. The whole time there is a constant positive pressure so any fluid-dynamics caused migration of TPE is into the healing wound, not out. I am convinced that TPE acts as a superthick fluid, which is why it you put her arm straight up then down nothing bad happens. Place her arm up and leave it there, eventually it will tear.
*snip*
The final touch that seems to work best, like Wheezer points out, is heat. This is where I've borked things that were almost healed!
I have 3 kinds of WM TPE to work with and all of them behave very differently with heat. My doll is almost too delicate for any, but a hot spoon has had the best results (I'll be checking out the mini iron, tyvm!).
My best experience with paste has been when it was closer to a fluid state, a bit like honey. Otherwise it will not bond well with my doll's TPE.
- Wheezer
- Doll Elder
- Posts: 2545
- Joined: Sat Dec 22, 2018 1:49 am
- Location: Wheezerville, USA
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
Super thick fluid ... perhaps.RevJack wrote: ↑Mon Aug 21, 2023 3:36 pm *snip*
Aside comment: When I paste the split in vaginas, I close the legs on the repair until the cure is done. The whole time there is a constant positive pressure so any fluid-dynamics caused migration of TPE is into the healing wound, not out. I am convinced that TPE acts as a superthick fluid, which is why it you put her arm straight up then down nothing bad happens. Place her arm up and leave it there, eventually it will tear.
*snip*
I think it just gets down to stress on the material.
TPE, rubber band, silicone, or whatever all react to stress or tension in different ways.
A rubber band wrapped around three pencils under low stress can hold for years.
That same band wrapped around a big can, and under significant stress, might only go a day without snapping.
The final material of a sex doll will depend on the base TPE hardness, any softening chemicals added and the coloring agent.
Like any flexible material it will reach a point where it fails. Either due to extreme tension, or long term lower level tension.
This can be mitigated to an extent by care for the TPE such as cleaning, oiling, avoiding certain chemicals or excessive UV light.
So with care and if kept in the neutral or as molded position, then the TPE should have a good long life.
NOTE:
I am omitting outliers such as "ultrasoft TPE" which has shown some ghastly stuff such as melting off of legs while a doll just stands there. That stuff REALLY acts like a super thick fluid.
TPE paste might look like a glue or a paste, but it is not.homersexual wrote: ↑Tue Nov 07, 2023 8:13 pm *snip*
That's been my experience with Vagina reconstruction. What has been the most effective is a TPE paste and some kind of object to keep the shape and provide opposing pressure to the TPE in the cavity against the partially closed legs. I keep my doll inverted, and the neutral internal pressure causes the TPE paste to creep into the surface fissures and bond, and the excess is pushed up out of the cavity and settles. I have used lots of TPE for this approach so that the legs don't have to be closed all the way and some of the tension is relieved.
The final touch that seems to work best, like Wheezer points out, is heat. This is where I've borked things that were almost healed!
I have 3 kinds of WM TPE to work with and all of them behave very differently with heat. My doll is almost too delicate for any, but a hot spoon has had the best results (I'll be checking out the mini iron, tyvm!).
My best experience with paste has been when it was closer to a fluid state, a bit like honey. Otherwise it will not bond well with my doll's TPE.
Rather it is inert TPE mixed with the 3M 94 bonding agent.
The thicker the TPE paste, the less 3M 94 and thus less bonding liquid.
So as the paste gets thicker, it bonding strength to base TPE decreases.
When I first concocted the paste it was designed for a specific purpose, how to repair TPE in a high stress areas.
Areas such breasts, thigh/leg repairs, etc. If you apply 3M 94 or heat to those areas under stress the TPE just unzips.
However a thick paste applied will fill in the area to relieve stress and the lower 3M 94 content will reduce unzipping.
Once that is cured a thinner paste containing more 3M 94 can be used for surface filling.
The thinner pasted bonds well and with the stress relieved and the TPE repair area does not unravel.
Over the years it seems to have morphed into the idea of a spackle or general repair glue.
To me 3M 94 TPE paste is an odd continuum.
At the thick end a good filler with for stress areas but less bonding strength to base TPE.
At the thin end a lower TPE content filler, thinner final skin and good bonding strength to base TPE.
You need to adjust the blend to meet your specific application.
And, as always, test it out first.
Hope it helps.
Cheers!
... W ...
Reason: Spelling correction in response to request from member.
- The Doll Advocate
- Doll Mentor
- Posts: 1684
- Joined: Wed Nov 23, 2022 8:30 pm
- Location: Texas
- Contact:
Re: TPE Breast Reduction at Reverend Jacks
Finally got you a hot knife ! I'm proud of you ! IRevJack wrote: ↑Mon Aug 21, 2023 3:36 pm After deep consultation with my business partner and therapist (Jack Daniel's), and a fly-by conversation with the love of my life (Mrs Reverend Jack) it was brought to my attention that there was just too much stress on the titties to pop back up. So paste is not going to work if the material is under separation stress.
Aside comment: When I paste the split in vaginas, I close the legs on the repair until the cure is done. The whole time there is a constant positive pressure so any fluid-dynamics caused migration of TPE is into the healing wound, not out. I am convinced that TPE acts as a superthick fluid, which is why it you put her arm straight up then down nothing bad happens. Place her arm up and leave it there, eventually it will tear.
So I decided to take a new tact, and try out a new toy, and I'm sealing the seams with heat. Here's my new toy:
20230821_152502.jpg
20230821_152521.jpg
20230821_152545.jpg
The foot is long enough to penetrate deep into the seam, so let's try and see if old Rev Jack can use the damn thing...
Re: TPE Breast Reduction at Reverend Jacks
Our website: https://www.coeros.com/
E-mail: service@coeros.com
Follow Coeros On: Youtube| Twitter | Reddit | Instagram
You can find related products on the official website, and related tutorials can be found in YouTube and TDF.